Item performance |
Test condition |
Test method |
Data unit |
Product designation |
||||||
|
2110G |
2120G |
2130G |
2130GB |
2710G |
2720G |
|||||
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
MPa |
90 |
140 |
160 |
150 |
105 |
150 |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
% |
6 |
7 |
7 |
7 |
7 |
9 |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
MPa |
130 |
185 |
200 |
180 |
130 |
180 |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
GPa |
2 |
3 |
4 |
4 |
2 |
3 |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
KJ/m2 |
40 |
50 |
50 |
45 |
40 |
65 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
KJ/m2 |
10 |
16 |
15 |
12 |
10 |
16 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
% |
10 |
20 |
30 |
30 |
10 |
20 |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
g/cm3 |
1.18 |
1.27 |
1.35 |
1.35 |
1.18 |
1.27 |
|
Molding shrinkage |
Dry state |
|
% |
--- |
--- |
--- |
--- |
--- |
--- |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
℃ |
257-262 |
245-258 |
245-256 |
245-256 |
257-262 |
245-258 |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
℃ |
245 |
245 |
247 |
247 |
245 |
245 |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
MV/m |
--- |
--- |
--- |
--- |
--- |
21 |
|
Volume resistivity |
Dry state |
GB/T1410 |
Ω.cm |
1014 |
1014 |
1014 |
1014 |
1014 |
7.8×1014 |
|
|
Other |
Water absorption |
|
|
% |
--- |
--- |
--- |
--- |
--- |
--- |
|
Flame retardant property |
Dry state |
UL94 |
|
HB |
HB |
HB |
HB |
HB |
HB |
|
Notes: the data is for reference only. Please consult our material engineers about specific use.
|
Item performance |
Test condition |
Test method |
Data unit |
Product designation |
||||||
|
2730G |
2730GB |
2735G |
2750G |
L2730G |
L2730GH |
|||||
|
Mechanical property |
Tensile strength |
23℃ (dry state) |
ISO527 |
MPa |
175 |
155 |
190 |
230 |
190 |
190 |
|
Elongation at break |
23℃ (dry state) |
ISO527 |
% |
8 |
7 |
8 |
7 |
6 |
6.5 |
|
|
Bending strength |
23℃ (dry state) |
ISO178 |
MPa |
210 |
200 |
240 |
300 |
290 |
290 |
|
|
Flexural modulus |
23℃ (dry state) |
ISO178 |
GPa |
5 |
5 |
5 |
8 |
8 |
8 |
|
|
Non-notched impact strength |
23℃ (dry state) |
ISO179 |
KJ/m2 |
105 |
60 |
100 |
110 |
105 |
105 |
|
|
Notch impact strength |
23℃ (dry state) |
ISO179 |
KJ/m2 |
25 |
15 |
20 |
25 |
20 |
20 |
|
|
Glass fiber content |
Dry state |
ISO3451 |
% |
30 |
30 |
35 |
50 |
33 |
33 |
|
|
Physical performance |
Specific gravity |
Dry state |
ISO1183 |
g/cm3 |
1.35 |
1.35 |
1.35 |
1.45 |
1.35 |
1.35 |
|
Molding shrinkage |
Dry state |
|
% |
--- |
--- |
1.0-1.5 |
--- |
--- |
--- |
|
|
Thermal performance |
Melting range |
Dry state |
ISO3146 |
℃ |
245-260 |
245-260 |
256-262 |
255-265 |
257-262 |
258-265 |
|
Thermal deformation temperature |
1.8Mpa |
ISO75 |
℃ |
250 |
245 |
247 |
247 |
254 |
258 |
|
|
Electrical performance |
Dielectric strength |
Dry state |
GB/T1408 |
MV/m |
18 |
17 |
22 |
23 |
--- |
--- |
|
Volume resistivity |
Dry state |
GB/T1410 |
Ω.cm |
1014 |
1014 |
1014 |
1014 |
1014 |
1014 |
|
|
Other |
Water absorption |
|
|
% |
--- |
--- |
--- |
--- |
--- |
--- |
|
Flame retardant property |
Dry state |
UL94 |
|
HB |
HB |
HB |
HB |
HB |
HB |
|
Notes: the data is for reference only. Please consult our material engineers about specific use.